Most players prefer forged heads over cast due to its feel and sound at impact as they have a greater consistency in their grain structure compared to cast heads. Although due to the intensive heat and pressure during the forging process, the finest forged heads will have distortions in their microstructure. Each billet is heated up to 1200°C and hammered into shape by 1000ton force. Similar to how the Japanese samurai swords are quenched in water to obtain their strength, air cooling from such high temperature will also cause the grains to shrink and not reach its full potential. We re-heat each head again to austenite state and annealed over 72 hours in straw ash and this extra step is how we create the dense, premium and smooth feel we our renowned for. We are committed to delivering the highest and purest quality with our unsurpassable craftsmanship soul.

鍛造製法は鋳造に比べ、クラブの打感や音に直接影響する内部繊維の一貫性が圧倒的に優れている事から多くのプレーヤーに好まれるようになりました。しかし、そんな鍛造製法で作られたヘッドであっても1200℃の高温且つ1000トンもの圧力で成形されてしまうと、どうしても炭素と鉄が結合して作られる内部組織に歪みが生じてしまいます。また、真っ赤に熱した日本刀を一気に水で冷やして強度を持たす焼き入れと同様に、ゴルフクラブのヘッドも1200℃まで熱された状態から空冷されてしまうと内部組織が縮こまり、本来軟鉄が持つ粘りのある柔らかさが十分に発揮されません。FTラインでは、鍛造、研磨が全て済んだヘッドをもう一度熱し、鍛造工程で生じた内部組織の歪みを取り除く焼き鈍しを行っております。焼き鈍しとは、保温製に優れている藁灰や砂の中でゆっくり時間をかけて冷ましてあげる事により、内部組織をより均一で高密度な物にする工程です。最高なモノづくりには欠かせない手間を一切惜しまない職人精神に基づき、自信を持ってお届けします。

 

 
P@.png
9999.png
EX999.jpg

Worlds finest purity of iron content 99.99%.

The softness of carbon steel depends on the ratio of carbon content. The less carbon infused, the softer the steel becomes. S15C carbon steel in forged golf clubs that contain roughly 13 to 18% of carbon is considered the softest material that can be used. Golf clubs forged out of softer materials such as S10C are not able to sustain their loft and lie angle throughout it’s usage. Fujimoto is dedicated to product innovation and development. Our team is comprised of experts in golf club manufacturing and product designers to stay abreast of the industry of emerging and evolving. Our extensive R&D has resulted in the creation of QUAD NINE. Using the method of layering pure iron, it contains less than 0.01% carbon on a S20C carbon steel base material. With the feedback we received from top Japanese tour players, we preserved the pure iron feel to the finest level by replacing the hard layer of chrome plating with Japanese Black Oxide (Kurozome). Fujimoto’s QUAD NINE purity complies with the Japan Industrial Standard and is also the first in forged golf club history to accomplish the use of this holy grail metal. 99.99% purity ultra pure iron.

世界最高99.99%の超純鉄。

軟鉄炭素鋼の柔らかさは炭素の含有率で決まり、炭素が少ないほど鉄に柔らかさや粘りが生まれます。従来軟鉄鍛造製のゴルフクラブではS15C軟鉄炭素鋼が使用可能な最も柔らかい軟鉄とされてきました。S15Cは約13から18%の炭素含有率があり、これ以下のS10Cなどは使用して行く中でロフトやライ角が簡単に変形してしまう為、使用不可能でした。藤本ゴルフは幾度にわたる研究の末、従来不可能とされていた炭素含有率0.01%以下の超純鉄の使用に成功致しました(クアッドナイン製法)。開発においてツアーで戦うトッププロの意見も取り入れ、S20C軟鉄炭素鋼の母体と組み合わせる事で、今までに無い芯のある上質な柔らかさを実現しました。また、クラブの表面を硬質なクロームメッキで覆ってしまうと、せっかくの軟鉄素材の良さを十分に味わえない事もツアープロの間では良く知られております。クアッドナイン製法では、彼らの意見を取り入れ上質な超純鉄を少しでも多く堪能して頂けるように、あえてメッキは施さず黒染め加工で表面処理をさせて頂きました。